Polyaspartic Resin Flooring Solution

Total amine value (mg KOH/g)

195±10

Viscosity (mPa·s at 25°C)

950±300

Solid content (%)

>97.0

Super weather-resistant, chemical-resistant, wear-resistant, with excellent mechanical properties and strong adhesion.

Classic data for finished products:

23°C, 50% RH; open time: 30 min; Tack-free Time: 45 min; Hard Dry Time: 4 h; tensile strength: 20 MPa; elongation at break: 150%. A 1:1 ratio can be achieved by either mass or volume.

Recommended apps:

Water parks, rooftops, hospitals, and other applications involving lightweight elastic flooring; building renovation; metal protective coatings; and waterproofing for rail transit systems.

NCO content (%)

6.6±0.5

Viscosity (mPa·s at 25°C)

3100±500

Moisture (%)

—

Active ingredient (%)

>85.0

Total amine value (mg KOH/g)

195±10

Viscosity (mPa·s at 25°C)

950±300

Solid content (%)

>97.0

Super weather-resistant, chemical-resistant, wear-resistant, with excellent mechanical properties and strong adhesion.

Classic data for finished products:

23°C, 50% RH; open time: 30 min; Tack-free Time: 45 min; Hard Dry Time: 4 h; tensile strength: 20 MPa; elongation at break: 150%. A 1:1 ratio can be achieved by either mass or volume.

Recommended apps:

Waterproofing and repair of roofs and other building structures, as well as waterproofing for rail transit systems.

NCO content (%)

6.1±0.5

Viscosity (mPa·s at 25°C)

3000±500

Moisture (%)

—

Active ingredient (%)

>85.0

Total amine value (mg KOH/g)

222±10

Viscosity (mPa·s at 25°C)

260±100

Solid content (%)

>97.0

Super weather-resistant, chemical-resistant, wear-resistant, with excellent mechanical properties and strong adhesion.

Classic data for finished products:

23°C, 50% RH; open time: 30 min; Tack-free Time: 45 min; Hard Dry Time: 6 h; tensile strength: 20 MPa; elongation at break: 500%.

Recommended apps:

Water‑conservation dam waterproofing, wear‑resistant surface layer for synthetic running tracks, waterproofing and repair, and wind‑turbine leading‑edge protective coatings.

NCO content (%)

3.5±0.5

Viscosity (mPa·s at 25°C)

2500±500

Moisture (%)

—

Active ingredient (%)

>73.0

Total amine value (mg KOH/g)

170±10

Viscosity (mPa·s at 25°C)

300±200

Solid content (%)

>85.0

Weather-resistant, chemical-resistant, wear-resistant, with excellent mechanical properties and strong adhesion;

Classic data for finished products:

23°C, 50% RH; open time: 30 min;  Hard Dry Time: 8 h; tensile strength: 25 MPa; elongation at break: 10%; hardness reaches 70 D after 1 day. A 1:1 ratio can be achieved by either mass or volume.

Recommended apps:

The primer and topcoat for colored‑film flooring.

NCO content (%)

13.0±0.5

Viscosity (mPa·s at 25°C)

500±300

Moisture (%)

—

Active ingredient (%)

>85.0

Total amine value (mg KOH/g)

195±10

Viscosity (mPa·s at 25°C)

1000±300

Solid content (%)

>85.0

Weather-resistant, chemical-resistant, wear-resistant, with excellent mechanical properties and strong adhesion;

Classic data for finished products:

Finished product standard data: 23°C, 50% RH; open time: 120 min;  Hard Dry Time: 24 h; hardness after 4 days: 70 D.

Recommended apps:

Topcoats for self-leveling floors, garage floors, and other flooring surfaces.

NCO content (%)

13.0±0.5

Viscosity (mPa·s at 25°C)

500±300

Moisture (%)

—

Active ingredient (%)

>85.0

Total amine value (mg KOH/g)

170±10

Viscosity (mPa·s at 25°C)

500±300

Solid content (%)

>98.0

Weather-resistant, chemical-resistant, wear-resistant, with excellent mechanical properties and strong adhesion;

Classic data for finished products:

23°C, 50% RH; open time: 35 min;  Hard Dry Time: 24 h; hardness after 2 days: 70 D.

Recommended apps:

Universal floor finish.

NCO content (%)

13.0±0.5

Viscosity (mPa·s at 25°C)

900±300

Moisture (%)

—

Active ingredient (%)

>98.0