◣ Grout, construction projects, adhesives
| Product grade | Product Specifications | Characteristics and Applications | |||
| WS-G5401 | Total amine value mgKOH/g 195±5 |
Viscosity (mPa·s at 25°C) 1500±500 |
Moisture (%) <0.1 | Solid content (%) >99.0 |
In the field of aspartic polyurea grout, under conditions of 25°C and 50% relative humidity, the product’s application time is… |
| N6813 | NCO content (%) 13.5±0.5 |
Viscosity (mPa·s at 25°C) 3100±500 |
Moisture (%) — |
Solid content (%) >99.0 |
|
| WS-G5401 | Total amine value mg KOH/g 195±5 |
Viscosity (mPa·s at 25°C) 1500±500 |
Moisture (%) <0.1 | Solid content (%) >99.0 |
In the field of aspartic polyurea grout, at 25°C and 50% relative humidity, the product has a caulking time of 15–20 minutes and a scraping time of 2–3 hours, with rapid curing. |
| N6813 | NCO content (%) 13.5±0.5 |
Viscosity (mPa·s at 25°C) 3100±500 |
Moisture (%) — |
Active ingredient (%) >99.0 | |
| WS-G5402 | Total amine value mg KOH/g 185±5 |
Viscosity (mPa·s at 25°C) 800±300 |
Moisture (%) <0.1 | Solid content (%) >99.0 |
In the field of aspartic polyurea grout, at 25°C and 50% relative humidity, the product’s application time is 30–35 minutes, and the scraping time is 6–7 hours, providing ample working time and excellent flexibility. |
| N5630 | NCO content (%) 13.5±0.5 |
Viscosity (mPa·s at 25°C) 3100±500 |
Moisture (%) — |
Active ingredient (%) >99.0 |
|
| WS-G5405 | Total amine value mg KOH/g 190±5 |
Viscosity (mPa·s at 25°C) 500±300 |
Moisture (%) <0.1 | Solid content (%) >99.0 |
In the field of aspartic polyurea grouting sealant, under conditions of 25°C and 50% relative humidity, the product’s application time is 20–25 minutes, and the scraping time is 4–5 hours. The tensile strength can reach 20 MPa. |
| N5631 | NCO content (%) 14.5±0.5 |
Viscosity (mPa·s at 25°C) 2500±500 |
Moisture (%) — |
Active ingredient (%) >99.0 | |
| WS-G5402 | Total amine value mg KOH/g 185±5 |
Viscosity (mPa·s at 25°C): 800 ± 300 | Moisture (%) <0.1 | Solid content (%) >99.0 |
In the field of aspartic polyurea grout, at 25°C and 50% relative humidity, the product’s application time is 30–35 minutes, and the scraping time is 6–7 hours, providing ample working time and excellent flexibility. |
| N5630 | NCO content (%) 13.5±0.5 |
Viscosity (mPa·s at 25°C) 3100±500 |
Moisture (%) — |
Active ingredient (%) >99.0 | |
| WS-G5405 | Total amine value mg KOH/g 190±5 |
Viscosity (mPa·s at 25°C) 500±300 |
Moisture (%) <0.1 | Solid content (%) >99.0 |
In the field of aspartic polyurea grouting sealant, under conditions of 25°C and 50% relative humidity, the product’s application time is 20–25 minutes, and the scraping time is 4–5 hours. The tensile strength can reach 20 MPa. |
| N5631 | NCO content (%) 14.5±0.5 |
Viscosity (mPa·s at 25°C) 2500±500 |
Moisture (%) — |
Active ingredient (%) >99.0 | |
◣ Application Scenarios
| Product grade | Product Specifications | Characteristics and Applications | |||
| WS-G5406 | Total amine value, mg KOH/g: 170 ± 5 | Viscosity (mPa·s at 25°C) 2000±500 |
Moisture (%) < 0.1 | Solid content (%) >99.0 | In the field of polyurea grouting sealants, at 25°C and 50% relative humidity, the product’s application time is 20–25 minutes, and the scraping time is 4–5 hours. The product… |
| N5631 | NCO content (%) 15.0±0.5 |
Viscosity (mPa·s at 25°C) 4500±500 |
Moisture (%) — |
Active ingredient (%) >99.0 | Compared with the WS‑G5405+N5631, the adhesion performance has been improved. |
| WS-G5408 | Total amine value mg KOH/g 170±5 |
Viscosity (mPa·s at 25°C) 900±300 |
Moisture (%) <0.1 |
Solid content (%) >99.0 | In the field of polyurea grouts for tile joints, at 25°C and 50% relative humidity, the product’s application time is 20–25 minutes, while the scraping time is reduced to 2–3 hours, providing ample working time and rapid subsequent curing. |
| N5631 | NCO content (%) 15.0±0.5 |
Viscosity (mPa·s at 25°C) 4500±500 |
Moisture (%) — |
Active ingredient (%) >99.0 |
|
| WS-G5409 | Total amine value mg KOH/g 185±5 |
Viscosity (mPa·s at 25°C) 2800±500 |
Moisture (%) <0.1 | Solid content (%) >99.0 | In the field of polyurea grouts for tile joints, under conditions of 25°C and 50% relative humidity, the product’s application time is… |
| N5631 | NCO content (%) 15.0±0.5 |
Viscosity (mPa·s at 25°C) 4500±500 |
Moisture (%) — |
Active ingredient (%) >99.0 | Within 15–20 minutes, the scraping time can be reduced to 2 hours, significantly shortening the overall construction timeline. |
◣ Application Scenarios
◣ Beauty Gel
| Product grade | Product Specifications | Characteristics and Applications | |||
| Component A and Component B react in a volume ratio of 1:1. | |||||
| T7400 | Total amine value mgKOH/g 100±5 | Viscosity (mPa·s at 25°C) 800±200 |
Moisture (%) <0.1 |
Solid content (%) >99.0 | In the field of aspartic polyurea cosmetic adhesives, the product achieves surface dryness within 3–4 hours and exhibits excellent adhesion to substrates such as cement and glazed ceramics. |
| N6030 | NCO content (%) 8±0.5 |
Viscosity (mPa·s at 25°C) 6000±1000 |
Moisture (%) — |
Active ingredient (%) >99.0 |
|
Component A and Component B react in a volume ratio of 1:1. |
|||||
| T7100 | Total amine value, mg KOH/g: 51 ± 5 | Viscosity (mPa·s at 25°C) 1200±300 |
Moisture (%) < 0.1 | Solid content (%) > 99.0 | In the field of aspartic polyurea cosmetic adhesives, the product exhibits a surface-drying time of 2–3 hours under standard test conditions (25°C, 50% relative humidity). It maintains excellent adhesion and flexibility even at ultra-low temperatures of –20°C, and demonstrates strong adhesion to substrates such as cement, glass, and glazed ceramics. |
| N2030 | NCO content (%) 4.0 ± 0.5 | Viscosity (mPa·s at 25°C) 3800±500 |
Moisture (%) — | Active ingredient (%) >99.0 |
|
| Component A and Component B are mixed in a volume ratio of 1:2. | |||||
| B3700 | Total amine value mgKOH/g 97±5 |
Viscosity (mPa·s at 25°C) 6800±500 |
Moisture (%) <0.1 |
Solid content (%) >99.0 |
In the field of aspartic polyurea cosmetic adhesives, the product exhibits a surface-drying time of 4–5 hours under standard test conditions (25°C, 50% relative humidity) and demonstrates excellent adhesion to substrates such as cement, glass, and glazed ceramics. |
| N6031 | NCO content (%) 4.0±0.5 |
Viscosity (mPa·s at 25°C) 1700±500 |
Moisture (%) — |
Active ingredient (%) >99.0 | |
◣ Application Scenarios
◣ Polyurethane for Home Use
Previous post:
Next article:
Related Cases
Global Headquarters
Address: No. 21, Chongqing Avenue, Yantai Economic and Technological Development Zone, Shandong Province
Wanshun Official Account
Shunda Official Account
Wanchuang Official Account